High Temp Resin has a heat deflection temperature (HDT) of 238 °C @ 0.45 MPa — the highest among Formlabs resins.

Choose High Temp Resin to print detailed, precise prototypes and end use parts that require high thermal stability, such as molds and inserts, parts exposed to hot air, gas, and fluid flow, as well as heat-resistant mounts, housings, and fixtures.

Form 4(B)L print settings are in progress, view the settings roadmap to see when settings for this material will be available on the Form 4(B)L.

Why Choose High Temp Resin

Our best material for stability under heat, High Temp Resin offers the highest heat deflection temperature among Formlabs resins.

High Thermal Stability

High Temp Resin offers the highest heat deflection temperature of any Formlabs material.

Ease of Use

Formlabs' accessible technology makes it easy to experiment with high temperature applications.

Applications

With the highest Heat Deflection Temperature of any Formlabs material, High Temp Resin is ideal for applications that require resistance to high temperatures.

Hot air, gas, and fluid flow

Heat resistant mounts, housings, and fixtures

Molds and inserts

Material Properties

Green

Ultimate Tensile Strength: 21 MPa

Tensile Modulus: 0.75 GPa

Elongation at Break: 14%

Flexural Modulus: 0.7 GPa

Notched Izod: 33 J/m

Post-Cured at 60°C

Ultimate Tensile Strength: 58 MPa

Tensile Modulus: 2.8 GPa

Elongation at Break: 3.3%

Flexural Modulus: 2.6 GPa

Notched Izod: 18 J/m

Post-Processing

Form Wash Settings

Duration

6 min

Notes

Do not leave High Temp Resin in solvent for longer than 6 minutes total, as excessive solvent exposure affects the quality of the final part.

Form Cure Settings

Duration

120 min

Temperature

80 °C

Notes

There are several post-curing options for High Temp V2. Refer to the technical data sheet to understand how different options affect mechanical properties, and choose the post-cure option that is best suited to the intended application. To achieve the highest HDT of 238 °C @ 0.45 MPa: (1) Post-cure parts in Form Cure for 120 min at 80 °C. (2) Thermally post-cure parts in a non-food oven for 3 hours at 160 °C. For applications that do not require the maximum heat resistance, post-cure parts in Form Cure for 60 min at 60 °C.